TiAl 基合金固相焊接界面及其显微组织分析
黄伯云1; 贺跃辉1; 王彬1; 刘咏1;郭景杰2

(1.中南工业大学粉末冶金国家重点实验室; 长沙;410083;
2.哈尔滨工业大学材料学院
)

摘 要: 采用惰性气氛下热压方法,研究了 Ti-33Al-3CR(质量分数,%)合金粗大(α2/γ)层片组织材料/粗大(α2/γ)层片组织材料及粗大(α2/γ)层片组织材料/细小双态组织 (γ+α2/γ)材料焊接界面及其显微组织,以及随后的热处理退火制度对此界面的影响.试验结果表明,粗大(α2/γ)/粗大(α2/γ)界面的显微组织 特征受界面粗大层片状晶团位向的影响.此类界面经过1250℃退火,其显微组织变化不明显,但促使γ相等轴晶退火孪晶的形成;而经过1280℃退火,原焊接联接界面变宽,在(α2/γ)晶团界面上发生部分再结晶现象;而经过1350℃退火(Ti-33Al-3CR合金的Tα≈1305℃),整个联接件材料 发生重结晶,形成新的、粗大的全层片状组织,原焊接联接界面消失.采用细晶双态组织材料与粗大全层片状组织材料对焊,可得到良好的固态焊接结合面. 

 

关键字: TiAl基合金; 固态焊接; 超塑性/扩散焊接; 热处理; 显微组织

SOLID PHASE WELDING AND MICROSTRUCTURE ANALYSIS OF TiAl BASED ALLOY
Huang Baiyun1 He Yuehui1 Wang Bing1 Liu Yong1 Guo Jinjie2

1.State Key Laboratory for Powder Metallurgy,Central South University of Technology,Changsha,410083,China;
2.School of Material Science and Engineering,Harbin Institute of Technology,Harbin, China

Abstract:Through hot pressing in Ar atmosphere,the joining interfaces and their microstructures of coarse( α2/γ ) lamellar material/coarse( α2/γ ) lamellar material and coarse( α2/γ ) lamellar material/fine duplex( γ+α 2/γ ) material have been studied and the subsequent heat treatment has also been studied.Results show that coarse( α2/γ )/coarse( α2/γ ) interface and its microstructure characteristics are affected by the orientations of coarse( α2/γ ) along the interface.After annealing at 1250 ℃,the microstructure in the interface had little variation except for the formation of γ equiaxial annealing twins; after annealing at 1280 ℃,the interface was widened,and recrystallization occured in the boundaries of ( α2/γ ) colonies; after annealing at 1350 ℃,recrystallization occured on the whole joined material,new coarse fully lamellar microstructure formed and the original joining interface disappeared.Perfect joining interface can be obtained through joining of the duplex material with coarse fully lamellar material. 

 

Key words: TiAl based alloy; solid state joining; superplastic/diffusion welding; heat treatment; microstructure

中南大学学报(自然科学版)
  ISSN 1672-7207
CN 43-1426/N
ZDXZAC
中南大学学报(英文版)
  ISSN 2095-2899
CN 43-1516/TB
JCSTFT
版权所有:《中南大学学报(自然科学版、英文版)》编辑部
地 址:湖南省长沙市中南大学 邮编: 410083
电 话: 0731-88879765 传真: 0731-88877727
电子邮箱:zngdxb@csu.edu.cn 湘ICP备09001153号